> “Since ethanol is the main component of hand sanitizer, we believe it is possible to de-bond and recycle the adhesive by using hand sanitizer as a substitute in certain real-world situations,” Aida says.
These sorts of environmental impact blurbs are hilarious. What kind of scenario are they envisioning where someone wants to remove and reuse a specialized adhesive bonding PTFE parts to something, but don't have ethanol on hand and have to fall back to using hand sanitizer?
Interesting that it seems like the application method is to melt the glue:
> To test its adhesive strength, researchers first glued two untreated polytetrafluoroethylene (PTFE) plates by sandwiching molten CyclicFP-fmoc between them and letting it cool at room temperature for 10 min.
Also notable that the glue substance is reusable:
> Remarkably, a simple ethanol wash completely stripped CyclicFP-fmoc from the target PTFE plates, leaving no trace behind. The recovered adhesive proved repeatedly reusable, reliably maintaining its adhesive strength of ~1.2 ± 0.1 MPa across multiple cycles.
Perhaps hot glue guns are going to get an update ;)
I'm very impressed that they were able to use glue on PTFE for...approximately anything at all. That's impressive.
But I'd like to take this opportunity to present my semi-annual rant about hot glue, instead.
It's amazing stuff. It's similar to many other liquid adhesives in that you can stick things together with it (probably not PTFE, but...), and they stay pretty well stuck.
But it's got this really neat property that most other things lack: When used with non-porous surfaces, it's removable. A few drops of isopropyl alcohol will eek in between the glue and the surface it is stuck to. It stays solid, but basically just falls right off with no apparent mess.
...which makes it absolutely fantastic for temporary fixturing.
Like: Glue an accelerometer to the middle of the 3D printer bed for resonance tuning using a very thin layer of hot glue, and then just use a bit of isopropyl to take it off later. It's like it never happened.
I have a weird use case, but this is actually wildly useful to me.
I use teflon (sometimes nylon, but mostly teflon) painter pyramids/holders/etc, because i spray finish stuff that is very good at adhering to lots of things, and are acetone based - VOC compliance pretty much forced acetone into solvent based stuff. This in turn pretty much makes finishes melt into anything except PE, nylon, teflon, even if they wouldn't otherwise.
To keep the pyramids and things where i want them, i have magnets glued into them. But because it's PFTE, the magnets don't really stay adhered well, even with (currently) specialized adhesives and i end up regluing them after every few times, often before the project finishes.
What i really want is an adhesive like this one, where i can glue the magnets in, but also remove them after the project finishes, because i'll go soak the pyramids in solvent or something to clean them, but don't want to damage any magnet coatings.
I think it could also be used outside of making a part. For example you want to setup sensor on a surface but it's important not to damage the surface, like the outside of a boat. This would be excellent for that.
These sorts of environmental impact blurbs are hilarious. What kind of scenario are they envisioning where someone wants to remove and reuse a specialized adhesive bonding PTFE parts to something, but don't have ethanol on hand and have to fall back to using hand sanitizer?
[0] - https://www.thistothat.com
The truth is nowadays you can just choose your favorite brand and they almost certainly have a correct, and good, adhesive selector.
For example, for loctite, you should just use: https://www.henkel-adhesives-selector.com/
> To test its adhesive strength, researchers first glued two untreated polytetrafluoroethylene (PTFE) plates by sandwiching molten CyclicFP-fmoc between them and letting it cool at room temperature for 10 min.
Also notable that the glue substance is reusable:
> Remarkably, a simple ethanol wash completely stripped CyclicFP-fmoc from the target PTFE plates, leaving no trace behind. The recovered adhesive proved repeatedly reusable, reliably maintaining its adhesive strength of ~1.2 ± 0.1 MPa across multiple cycles.
Perhaps hot glue guns are going to get an update ;)
But I'd like to take this opportunity to present my semi-annual rant about hot glue, instead.
It's amazing stuff. It's similar to many other liquid adhesives in that you can stick things together with it (probably not PTFE, but...), and they stay pretty well stuck.
But it's got this really neat property that most other things lack: When used with non-porous surfaces, it's removable. A few drops of isopropyl alcohol will eek in between the glue and the surface it is stuck to. It stays solid, but basically just falls right off with no apparent mess.
...which makes it absolutely fantastic for temporary fixturing.
Like: Glue an accelerometer to the middle of the 3D printer bed for resonance tuning using a very thin layer of hot glue, and then just use a bit of isopropyl to take it off later. It's like it never happened.
I use teflon (sometimes nylon, but mostly teflon) painter pyramids/holders/etc, because i spray finish stuff that is very good at adhering to lots of things, and are acetone based - VOC compliance pretty much forced acetone into solvent based stuff. This in turn pretty much makes finishes melt into anything except PE, nylon, teflon, even if they wouldn't otherwise.
To keep the pyramids and things where i want them, i have magnets glued into them. But because it's PFTE, the magnets don't really stay adhered well, even with (currently) specialized adhesives and i end up regluing them after every few times, often before the project finishes.
What i really want is an adhesive like this one, where i can glue the magnets in, but also remove them after the project finishes, because i'll go soak the pyramids in solvent or something to clean them, but don't want to damage any magnet coatings.
Yes, plenty. Especially if it sticks well while needed, and then can be non-destructively undone when no longer needed.